电熔莫来石：电熔莫来石采用高纯度石英砂，工业氧化铝，在超大电弧炉上熔炼而成，色泽较白，残炭极低，针状晶体发育良好，抗折强度大，它具有膨胀均匀，热稳定性能极好，荷重软化点高，高温蠕变值小，硬度大，搞化学腐蚀好等特点，广泛用于玻璃窑体炉衬砖，大型炼铁炉热风炉砖，陶瓷窑具，匣钵，棚板，石油化工等行业，是高档耐火材料的原材料。现根据市场需求开发种牌号：a莫来石-Ⅰ，b莫来石-Ⅱ,年生产能力3000吨，可根据用户需要加工各种规格产品。
Manufactured from pure quartz sand and industrialalumina in super-large electric arc furnace.. Fused Mullite has a high content of mullite crystals which confer high melting point ,excellent themal stability, low reversible themal expansion and resistance to themal shock and chemical corrosion at high temperature. It is widely used as lining bricksin glass body kiln and large hot wind furnace in iron-making blast furnace, as well as in ceramic liln and petrochemistry.

电熔锆莫来石：电熔法生产的锆莫来石，具有导热性能好、热膨胀系数小、抗渣性能强等特点，主要用于新型的浇钢滑板、连铸包的定径水口及长水口，玻璃窑炉的关键部位，其理化指标已达到了国内外同类产品水平，根据市场需要开发了三种锆含量不同的产品，年生产能力2500吨，可根据用户需要加工各种规格产品。
Manufactured from high quality raw materials in large electric arc furnace, Fused Zigconia Mullite has low reversible themal expansion ,excellent resistance to cracking , it can be used in continous casting expendables kiln furniture,nozzle brick ,etc.

电熔白刚玉：本厂采用大型电弧炉生产的白刚玉，晶体好，体积密度大，纯度高，有良好的耐高温，耐酸碱腐蚀性能，适用于研磨，抛光材料，精密铸造，喷涂材料，化工触媒载体，特种陶瓷。高级耐火材料等。根据指标可分为两种；普通白刚玉（Ⅰ）和低钠白刚玉（Ⅱ）：可根据用户需要加工各种规格段砂，粒度号砂及细粉，年生产能力4000吨。
Manufactured in the large electric arc fumace.White Fused Alumina (main crystalline phase a-AL2O3)is resistant to acid and alkali as well possess good property of resistance to abrasion .erosion and of volume stability at high temperature. It can be used in corundum brick. Corundum casket. Mullets corundum casket, slides shifting board,sliding brick ,corundum perforated brick refined out of furnace.whole sproy gun and composite smelting.cave fumace material of high temperature industry corundum castable masses etc.

电熔铝镁尖晶石：采用高纯正国烧镁和工业氧化铝在大型冶炼炉中生产的尖晶石，具有体积密度大、光泽好、抗侵蚀能力强、热稳定性能好等特点、广泛应用于炼钢电炉顶、转炉及电炉钢包、有色冶炼炉、水泥工业的回转窑过渡带和玻璃窑的蓄热室等。根据用户需要可分为70%、85%、90%三种氧化铝含量不同的尖晶石熟料及尖晶石固熔体，年生、产能、力2000吨，可根据用户需要加工各种规格产品。
Manufactured fron high purity raw materials in large electric arc furnace. Fused Magnesium Aluminum Spinal has excellent refractory properties and superion refractory aggregate. It can be used in aluminous refractory bodied .prefired shape and monolithics to improve their resistance to slag attack.